General Information
Features •Flammability •High Viscosity •Easy Release
Uses •Fire Resistance
Appearance •Clear/Transparent
Forms •Pellets
Processing Method •Extrusion •Injection Molding

Minimum Order Quantity 25kg

Packaging Details 25kg/bag

Delivery Time 3-5 working days to departure port

Supply Ability 1000MT/Month

Price $1.5-$3

Consult Now

Detail

CLARNATE®FR3710T
		Technical Data Sheet
Revision Date： 2021-03-01				NO .WHPCBU_0001
Name :	FR3710T			Version：3.0
CLARNATE®FR3710T Polycarbonate Resin
		General Information
Features		·Flammability	·High Viscosity	·Easy Release
Uses		·Fire Resistance
Appearance		·Clear/Transparent
Forms		·Pellets
Processing Method		·Extrusion	·Injection Molding
		Typical Properties
		Test Method	Test Condition	Unit
Physical
Melt Flow Index		ASTM D1238	300℃/1.2Kg	g/10min
Mold Shrinkage		ASTM D955	-	%
WaterAbsorption		ASTM D570	23℃,24h	%
Density		ASTM D792	-	g/cm³
Mechanical
Stress at Break		ASTM D638	50mm/min	MPa
Tensile Modulus		ASTM D638	1mm/min	MPa
Yield Stress		ASTM D638	50mm/min	MPa
Strain at Break		ASTM D638	50mm/min	%
Flexural Strength		ASTM D790	2mm/min	MPa
Flexural Modulus		ASTM D790	2mm/min	MPa
Izod Notched Impact Strength		ASTM D256	23℃	J/m
Thermal
Heat Distortion Temp.		ASTM D648	1.82MPa;3.2mm	℃
Vicat Softening Temp.		ASTM D1525	120℃/h;50N	℃
Date of issue: Mar. 01, 2021				CLARNATE®
Version： 3.0
			1 / 3

CLARNATE®FR3710T
	Typical Properties
	Test Method	Test Condition	Unit	Typical Value
Optical
Haze	ASTM D1003	3mm	%	<0.8
Light Transmittance	ASTM D1003	3mm	%	87
Flammability
	UL 94	1.5mm	-	V0
Processing Condition
Drying Temperature			℃	120
Drying Time			h	5
Injection Temperature			℃	280-300
Mold temperature			℃	80
For more information about safety and environment, please refer to our MSDS or contact our
customer service center.